PVD İşleme Özellikleri

PVD processing characteristics  

1) PVD film can be directly plated on stainless steel and hard alloy, the relatively soft zinc alloy, copper, iron and other die castings should be chemical electroplating chromium, and then suitable for PVD plating, but PVD easy to bubble after water plating, high defect rate;
2). Tipik PVD kaplama işleme sıcaklığı 250 derece ile 450 derece arasındadır;
3) kaplama tipi ve kalınlığı işlem süresini belirler, genel işlem süresi 36 saattir;
4). PVD coating film thickness is micron level, the thickness is relatively thin, generally 0.3μm 5μm, which decorative coating film thickness is generally 0.3μm1μm, so it can almost not affect the original size of the workpiece to improve the physical and chemical properties of the workpiece surface, and can maintain the workpiece size is basically unchanged, No reprocessing after plating;
5). PVD teknolojisi yalnızca kaplama ve matris malzemesinin yapışma gücünü iyileştirmekle kalmaz, aynı zamanda birinci nesil TiN'den TiC, TiCN, ZrN, CrN, MoS2, TiAlN, TiAlCN, Kalay-AlN, CNx'e kadar kaplama bileşimini geliştirir. , DLC ve TA-C ve farklı renk yüzey efektleri oluşturan diğer çoklu kompozit kaplamalar.
6). Film tabakasının mevcut rengi, koyu altın sarısı, açık altın sarısı, kahverengi, bronz, gri, siyah, gri-siyah, yedi renk vb. olabilir. Kaplama işleminde ilgili parametreler kontrol edilerek renk kontrol edilebilir. Kaplamanın bitiminden sonra, ilgili cihazın renk değerini ölçmek için kullanılabilir, böylece kaplama renginin gereksinimleri karşılayıp karşılamadığını belirlemek için renk ölçülebilir.